RESUMO
Surface coating has become an effective approach to improve the electrochemical performance of Ni-rich cathode materials. In this study, we investigated the nature of an Ag coating layer and its effect on electrochemical properties of the LiNi0.8Co0.1Mn0.1O2 (NCM811) cathode material, which was synthesized using 3 mol.% of silver nanoparticles by a facile, cost-effective, scalable and convenient method. We conducted structural analyses using X-ray diffraction, Raman spectroscopy, and X-ray photoelectron spectroscopy, which revealed that the Ag nanoparticle coating did not affect the layered structure of NCM811. The Ag-coated sample had less cation mixing compared to the pristine NMC811, which could be attributed to the surface protection of Ag coating from air contamination. The Ag-coated NCM811 exhibited better kinetics than the pristine one, which is attributed to the higher electronic conductivity and better layered structure provided by the Ag nanoparticle coating. The Ag-coated NCM811 delivered a discharge capacity of 185 mAh·g-1 at the first cycle and 120 mAh·g-1 at the 100th cycle, respectively, which is better than the pristine NMC811.
RESUMO
Elemental doping for substituting lithium or oxygen sites has become a simple and effective technique to improve the electrochemical performance of layered cathode materials. Compared with single-element doping, this work presents an unprecedented contribution to the study of the effect of Na+/F- co-doping on the structure and electrochemical performance of LiNi1/3Mn1/3Co1/3O2. The co-doped Li1-zNazNi1/3Mn1/3Co1/3O2-zFz (z = 0.025) and pristine LiNi1/3Co1/3Mn1/3O2 materials were synthesized via the sol-gel method using EDTA as a chelating agent. Structural analyses, carried out by X-ray diffraction, Raman spectroscopy, and X-ray photoelectron spectroscopy, revealed that the Na+ and F- dopants were successfully incorporated into the Li and O sites, respectively. The co-doping resulted in larger Li-slab spacing, a lower degree of cation mixing, and the stabilization of the surface structure, which substantially enhanced the cycling stability and rate capability of the cathode material. The Na/F co-doped LiNi1/3Mn1/3Co1/3O2 electrode delivered an initial specific capacity of 142 mAh g-1 at a 1C rate (178 mAh g-1 at 0.1C), and it maintained 50% of its initial capacity after 1000 charge-discharge cycles at a 1C rate.
Assuntos
Fontes de Energia Elétrica , Lítio , Ânions , Cátions , Eletrodos , Lítio/química , OxigênioRESUMO
This work aimed at synthesizing MoO3 and MoO2 by a facile and cost-effective method using extract of orange peel as a biological chelating and reducing agent for ammonium molybdate. Calcination of the precursor in air at 450 °C yielded the stochiometric MoO3 phase, while calcination in vacuum produced the reduced form MoO2 as evidenced by X-ray powder diffraction, Raman scattering spectroscopy, and X-ray photoelectron spectroscopy results. Scanning and transmission electron microscopy images showed different morphologies and sizes of MoOx particles. MoO3 formed platelet particles that were larger than those observed for MoO2. MoO3 showed stable thermal behavior until approximately 800 °C, whereas MoO2 showed weight gain at approximately 400 °C due to the fact of re-oxidation and oxygen uptake and, hence, conversion to stoichiometric MoO3. Electrochemically, traditional performance was observed for MoO3, which exhibited a high initial capacity with steady and continuous capacity fading upon cycling. On the contrary, MoO2 showed completely different electrochemical behavior with less initial capacity but an outstanding increase in capacity upon cycling, which reached 1600 mAh g-1 after 800 cycles. This outstanding electrochemical performance of MoO2 may be attributed to its higher surface area and better electrical conductivity as observed in surface area and impedance investigations.
RESUMO
An amorphous MomO3m-1/carbon nanocomposite (m ≈ 5) is fabricated from a citrate-gel precursor heated at moderate temperature (500 °C) in inert (argon) atmosphere. The as-prepared Mo5O14-type/C material is compared to α-MoO3 synthesized from the same precursor in air. The morphology and microstructure of the as-prepared samples are characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), and Raman scattering (RS) spectroscopy. Thermal gravimetry and elemental analysis indicate the presence of 25.8 ± 0.2% of carbon in the composite. The SEM images show that Mo5O14 is immersed inside a honeycomb-like carbon matrix providing high surface area. The RS spectrum of Mo5O14/C demonstrates an oxygen deficiency in the molybdenum oxide and the presence of a partially graphitized carbon. Outstanding improvement in electrochemical performance is obtained for the Mo5O14 encapsulated by carbon in comparison with the carbon-free MoO3.
RESUMO
Silver nanoparticles (AgNPs) and silver/quartz nanocomposite (Ag/Q)NPs)) were synthesized by sol-gel method using table sugar as chelating agent. The synthesized nanosized materials were used for mercury ions adsorption from aqueous solutions. The materials were characterized by X-ray diffraction (XRD), Transmission Electron microscope (TEM), and surface area (BET). Adsorption of Hg2+ (10 mg/l) is strongly dependent on time, initial metal concentration, dose of adsorbent and pH value. Silver/quartz nanocomposite ((Ag/Q)NPs)) shows better efficiency than individual silver nanoparticles (AgNPs). This composite removed mercury ions from the aqueous solution with efficiency of 96% at 60 min with 0.5g adsorbent dosage at pH 6. The adsorption process explained well by the pseudo-second-order kinetic model. In conclusion silver/quartz nanocomposite (Ag/Q)NPs)) shows higher removal efficiency for mercury ions from aqueous solutions than individual silver naoparticles (AgNPs) or quartz (Q).